EMERGE™ PC/ABS 7502
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lbI5XE_EMERGE-PC-ABS-7502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMERGE™ PC/ABS 7502 is a non-halogen ignition resistant 20% glass filled PC/ABS resin. It combines the superior physical properties of PC and the excellent processability of ABS. EMERGE PC/ABS 7502 is designed with excellent flow and high rigidity, outstanding capability in chemical resistance for use in internal structural parts of OA machine particular those, parts with thin wall thickness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.15 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ASTM D638 |
| Tensile Strength (Break) | 101 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 6200 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact | 380 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 112 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.500 mm | V-2 | ||
| 1.00 mm | V-1 | ||
| 1.20 mm, Black and White | V-0 | ||
| 1.50 mm 2 | V-0 | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 6550 | BASF Corporation | PBT | Ultradur® |
| VAMPALLOY 0024 V0 11 | Vamp Tech | PC+ABS | VAMPALLOY |
| Nucrel® 3990L | DuPont Packaging & Industrial Polymers | EAA | Nucrel® |
| ESPRENE EPDM 606F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Karina CLEAR PVC COMPOUND -E 80/314-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |