NYCOA Polyamide GR30 V0 Black
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lb9Die_NYCOA-Polyamide-GR30-V0-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA GR30 V0 is a 30% glass fiber reinforced, flame retardant Nylon 6 resin used for injection molding. This resin complies with ROHS requirements, as it contains a non-halogenated flame retardant package. NYCOA GR30 V0 is listed by Underwriters Laboratories as UL 94 V0 at 1.4mm thickness. Typical applications include speaker baskets, relay housings, bobbins, and electrical connectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.95 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 146 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3 | 9150 | MPa | ASTM D790 |
| Flexural Strength 4 | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 910 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.40 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 243 - 282 | °C | |
| Front Temperature | 254 - 291 | °C | |
| Nozzle Temperature | 252 - 291 | °C | |
| Processing (Melt) Temp | 254 - 291 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ SK3731 | Idemitsu Kosan Co., Ltd. | PC+AS | TARFLON™ |
| TOTAL Polypropylene PPC 4170 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Wondel® T TR0 | Nanjing Julong Engineering Plastics Co., LTD | PBT | Wondel® T |
| Forprene® 6SD001A85 | SO.F.TER. SPA | TPV | Forprene® |
| Karina WHITE COLOR CONCENTRATE 10/4-GI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |