Hanwha Total PP GH43
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lade11_Hanwha-Total-PP-GH43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GH43 is a G/F modified polypropylene compound modified by glass fiber filling to improve mechanical rigidity and heat-resistance. It is produced by modifying a variety of base PPs, including HIPP (High Isotactic Polypropylene), with Hanwha's special processing technology. Its excellent quality makes it ideal for use in air conditioner fans and automobile cooling fans; and like products requiring high rigidity and high impact-resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 0.20 - 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Apparent Bending Modulus | 147 | MPa | ASTM D747 |
| Flexural Modulus 3 | 5880 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 163 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 220 | °C | |
| Middle Temperature | 180 - 220 | °C | |
| Front Temperature | 180 - 220 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 49.0 - 88.3 | MPa | |
| Back Pressure | 0.490 - 0.981 | MPa | |
| Screw Speed | 30 - 80 | rpm |
| Injection instructions |
|---|
| Injection Speed: max |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN P20 D | Arkema | Nylon 11 | Rilsan® |
| RTP 6001-70A | RTP Company | TPE | RTP |
| Sylvin 8736-77 Grey 9453 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VESTAMID® HTplus M1033 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| Chemlon® 143 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |