AKROLOY® PA ICF 20 black (5268)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | laNRi5_AKROLOY-PA-ICF-20-black-5268-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced polyamide blend with high stiffness, good sliding properties and reduced moisture. Application areas are mechanically high stressed parts with dimensional stability and moisture independent properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.23 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 44.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | -- | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | -- | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 250 | -- | MPa | ISO 178 |
| Flexural Strain at Break 3 | 2.6 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 20 | -- | % | ISO 1172 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 6.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 45 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 223 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 255 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+5 | 1.0E+5 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® 3K3F NAT005 | SO.F.TER. SPA | PP Copolymer | Tecnoprene® |
| Clariant Nylon 6/6 66G25M15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ENPRENE 655 | En Chuan Chemical Industries Co,. Ltd. | SBS | ENPRENE |
| Sylvin 9812-60 Grey 9562 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-LOY™ A30009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |