Sindustris PC GN1009RF
| Category: | PC , Polycarbonate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | laGsFO_Sindustris-PC-GN1009RF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC GN1009RF is a Polycarbonate (PC) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC GN1009RF are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 60.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 96.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 780 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 103 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.600 mm | V-0 | ||
| 0.800 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 95.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 245 to 260 | °C | |
| Middle Temperature | 260 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 270 to 285 | °C | |
| Processing (Melt) Temp | 245 to 285 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 0.600 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PCSF-FR | Polymer Resources Ltd. | PC | PRL |
| TEREZ PA 6.6 7510 GF 25 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Mylar® S (92 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| NuSil CV2-2640 | NuSil Technology | Silicone | NuSil |
| Braskem PP F1000HC | Braskem America Inc. | PP, High Crystal | Braskem PP |