Tritheva® TN 8093
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Tritheva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | laGRvV_Tritheva-TN-8093.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tritheva®TN 8093 is an ethylene vinyl acetate copolymer (EVA) material,. This product is available in Latin America and is processed by film extrusion or co-extrusion. Tritheva®The main features of TN 8093 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 11.0 - 13.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 5.00 | MPa | ASTM D638 |
| Fracture, molding | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 660 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 53.0 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 55.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 32.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 33.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 460 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 760 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 430 | g | ASTM D1709B |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 96.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, 50.0 µm, blown film | 84 | ASTM D2457 | |
| 60, 50.0 µm, blown film | 132 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 1.7 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 0.30 to 0.50 g/10 min |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 - 150 | °C | |
| Cylinder Zone 2 Temp. | 140 - 155 | °C | |
| Cylinder Zone 3 Temp. | 155 - 170 | °C | |
| Adapter Temperature | 170 - 190 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AB605C | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| RTP ESD C 200.5 | RTP Company | Nylon 66 | RTP |
| RheTech Polypropylene F37-01UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Silplus® 80 HS | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Akulon® Ultraflow K-FHG12 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |