Petrothene® NA963
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | laDGON_Petrothene-NA963.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications: PETROTHENE NA963 is a series of resins formulated with special antiblock additive and designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA963 exhibits uniformity, ease of processing and good tensile strength. Regulatory Status: The basic resin NA963 meets the requirements of the Food and Drug Administration, 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for further information regarding the suitability of specific products for specific applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 10.7 | MPa | ASTM D638 |
| Fracture | 11.4 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 100 | % | ASTM D638 |
| Fracture | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm | 179 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm | 221 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 23.4 | MPa | ASTM D882 |
| TD : Yield, 32 µm | 16.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 160 | % | ASTM D882 |
| TD : Broken, 32 µm | 480 | % | ASTM D882 |
| Dart Drop Impact (32 µm) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 300 | g | ASTM D1922 |
| TD : 32 µm | 180 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 154 - 177 | °C |
| Extrusion instructions |
|---|
| Generally recommended extrusion conditions include a melt temperature range of 310°-350°F (155°-177°C) and a blow-up ratio range of 1.8-2.5:1. Drawdown to gauges below 1.0 mils (<25 microns) is possible at commercial rates when proper techniques are used. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1311 | RTP Company | PPS | RTP |
| Sylvin 8280-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nipol® 1051 | Zeon Chemicals L.P. | NBR | Nipol® |
| Adell PP RR-17 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| EcoLon® 2000-BK1 | Wellman Engineering Resins | Nylon 66 | EcoLon® |