TECHNYL® C 442 BLACK V
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | la4N71_TECHNYL-C-442-BLACK-V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced polyamide PA6, high viscosity, with high flexibility and very high impact resistance even at low temperature, for extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 900 | 400 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 35.0 | 30.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 220 | 270 | % | ISO 527-2/1A |
| Flexural Modulus | 850 | 380 | MPa | ISO 178 |
| Flexural Stress | 40.0 | 20.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | No Break | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 85 kJ/m² | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.12 | IEC 60250 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Cylinder Zone 1 Temp. | 200 to 210 | °C | |
| Cylinder Zone 3 Temp. | 210 to 220 | °C | |
| Cylinder Zone 5 Temp. | 210 to 220 | °C | |
| Die Temperature | 220 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIC3702 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Semi-Rigid | Sinvicomp |
| NORYL PPX™ PPX7110 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |
| APEX® 90-R471U-80-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| CP PRYME® Polystyrene PS100BT-8M CLEAR | Chase Plastics Services Inc. | PS (GPPS) | CP PRYME® Polystyrene |
| HIVAL® 2635 | Nexeo Solutions, LLC. | PP Impact Copolymer | HIVAL® |