LNP™ LUBRICOMP™ WL003 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lZthZI_LNP-LUBRICOMP-WL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WL003 is a compound based on PBT resin containing 15% PTFE. Added feature of th is grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound WL-4030 Product reorder name: WL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 3.0 | % | |
| Across Flow : 24 hr | 2.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2780 | MPa | ASTM D638 |
| -- | 2870 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 47.2 | MPa | ASTM D638 |
| Yield | 47.2 | MPa | ISO 527-2/5 |
| Break 3 | 47.1 | MPa | ASTM D638 |
| Break | 47.1 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.5 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2/5 |
| Break 5 | 7.8 | % | ASTM D638 |
| Break | 6.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2190 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.24 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor - Washer | 20.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 8 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 9 | 27 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 0.800 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 177 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 159 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 58.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 62.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PE HDPE-0149 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Ferro PP LPP26BC63UL-BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| EPO-TEK® 301-2FL | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HiFill® PA6 IM 40 Z | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Sylvin 9812-65 Brown 7419 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |