Kepital® FL2020
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lZgeQe_Kepital-FL2020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium-high viscosity grade for general injection molding. It was modified with 20% PTFE powder, and so suitable for parts requiring low wear and friction. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 5.0 | g/10 min | ASTM D1238 |
| -- | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00 mm | 2.1 | % | ASTM D955 |
| 3.00 mm | 2.1 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 44.0 | MPa | ASTM D638 |
| Yield, 23°C | 45.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2100 | MPa | ASTM D790 |
| 23°C | 2150 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 65.0 | MPa | ASTM D790 |
| 23°C | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 16 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 HL NTLA010 NT308 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Anjacom® 250-H/GF50 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Evermore PUR SA-2130M | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| DINALON® B1S25 M (Black) | Grupo Repol | Nylon 6 | DINALON® |
| Lumid® GP2500B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |