FUDOWLITE® FC3450
| Category: | Phenolic , Phenolic |
| Manufacturer: | Fudow Co., Ltd. |
| Trademark: | FUDOWLITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lZI5kI_FUDOWLITEFC3450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Examples of application
Other properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 - 1.37 | g/cm³ | JIS K7112 |
| Apparent Density | 4.50 | g/cm³ | |
| Molding Shrinkage | 0.80 - 1.1 | % | JIS K6911 |
| Water Absorption (23°C, 24 hr) | 0.30 - 0.40 | % | JIS K6911 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 105 | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 49.0 - 69.0 | MPa | JIS K6911 |
| Flexural Modulus | 6370 - 7350 | MPa | JIS K7171 |
| Flexural Stress | 59.0 - 78.0 | MPa | JIS K7171 |
| Compressive Stress | 186 - 206 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.9 - 5.9 | kJ/m² | JIS K7111 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 6.0E-5 | cm/cm/°C | |
| Heat Deflection Temperature | 150 - 160 | °C | JIS K7191-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | JIS K6911 | ||
| after boiling | 1.0E+8 - 1.0E+9 | ohms | JIS K6911 |
| at ordinary state | 1.0E+10 - 1.0E+11 | ohms | JIS K6911 |
| Dielectric Strength | 10 - 12 | kV/mm | JIS K6911 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1399 X 91176 | RTP Company | PPS | RTP |
| PREMIER™ A240-HTHF | Chomerics, div. of Parker Hannifin Corp. | PC+ABS | PREMIER™ |
| RTP 301 TFE 10 | RTP Company | PC | RTP |
| 3M™ Dyneon™ PTFE TF 1750 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| FHR Polypropylene P6C6B-134 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |