PENTALLOY BS 6 H RC UV black
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + PA |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTALLOY BS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lXG44S_PENTALLOYBS6HRCUVblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA-ABS alloy recompound, unreinforced, heat stabilised |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.7 | -- | % | ISO 294-4 |
| Flow | 1.5 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 3.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1850 | -- | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | |||
| Yield | 50.0 | -- | MPa | ISO 527-2/50 |
| Fracture | 45.0 | -- | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 3.5 | -- | % | ISO 527-2/50 |
| Fracture | > 70 | -- | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 65 | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 110 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 27 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.10 | -- | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.070 - 0.15 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 255 - 280 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 245 - 285 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 50.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® RP 2001-C | Plastic Solutions, Inc. | PP Random Copolymer | PrimaFlex® |
| DURACON® HP25X | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Hyrene® PS-MI 14/1.3 | Entec Polymers | PS (MIPS) | Hyrene® |
| Plaslube® PA6 GF20 RM L BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| NORYL™ PX9406P resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |