Lucky Enpla LAY1003HM
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lXCkxb_Lucky-Enpla-LAY1003HM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucky Enpla LAY1003HM is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Lucky Enpla LAY1003HM applications include home applications and coating applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 58.8 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2220 | MPa | ASTM D790 |
| Flexural Strength 3 | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 113 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Nozzle Temperature | 250 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 250-270°CInjection Pressure (1st Pressure): 800-1200 kg/cm²Injection Pressure (2nd Pressure): 300-700 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-709S | CHI MEI CORPORATION | ABS | POLYLAC® |
| megol® PUG 60 | API SpA | SEBS | megol® |
| Taitarex® 818K | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |
| POLIMAXX 3342S | IRPC Public Company Limited | PP Random Copolymer | POLIMAXX |
| Thermec N™ 4314R60H Bk-1 | Technical Polymers, LLC | PPA | Thermec N™ |