Durethan® DP 2325 H3.0 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lWidgL_Durethan-DP-2325-H3-0-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, non-reinforced, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 1.6 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.20 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 2.1 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.50 | -- | % | |
| Across Flow : 280°C, 3.00 mm 5 | 1.9 | -- | % | |
| Across Flow : 120°C, 4 hr, 3.00 mm 6 | 0.10 | -- | % | |
| Flow : 280°C, 3.00 mm 7 | 2.1 | -- | % | |
| Flow : 120°C, 4 hr, 3.00 mm 8 | 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | 700 | MPa | ISO 527-2/1 |
| Tensile Stress | ||||
| Yield, 23°C | 50.0 | 30.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 47.0 | 49.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ||||
| Yield, 23°C | 21 | 38 | % | ISO 527-2/50 |
| Break, 23°C | 80 | 290 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 50 | 50 | % | ISO 527-2/50 |
| Flexural Modulus 9(23°C) | 1700 | 660 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 55.0 | 19.0 | MPa | |
| 23°C 10 | 70.0 | 27.0 | MPa | |
| Flexural Strain at Flexural Strength 11(23°C) | 7.2 | 8.7 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 12(> 1.00 mm) | 25 | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66-HI, GHR, 14-020 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | 20 | kJ/m² | |
| 23°C | 50 | 100 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 25 | 20 | kJ/m² | |
| 23°C | 80 | 100 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 60.0 | -- | J | |
| 23°C | 50.0 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 5400 | -- | N | |
| 23°C | 3900 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 110 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 13 | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.3E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+19 | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 40 | 45 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 3.50 | 7.00 | ||
| 23°C, 1 MHz | 3.00 | 3.40 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 8.0E-3 | 0.15 | ||
| 23°C, 1 MHz | 0.015 | 0.075 | ||
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 14 | 20 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 150x105x3mm, 80°C MT, 500 bar |
| 6 . | 150x105x3mm |
| 7 . | 150x105x3mm, 80°C MT, 500 bar |
| 8 . | 150x105x3mm |
| 9 . | 2.0 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | 2 mm/min |
| 12 . | US-FMVSS302 |
| 13 . | 10°C/min |
| 14 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 8 APFLM/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| ARBOBLEND® V5 | TECNARO GmbH | Biodeg Polymers | ARBOBLEND® |
| IDI SMC S30 (Glass Content 30%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Lifolit® SG 53.1380/1 HT | ELASTO | PVC, Flexible | Lifolit® |
| POLYFORT® FPP 2181 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |