HIPREN® EM 1712 T TDAE
| Category: | SBR, Emulsion , Emulsion Styrene Butadiene Rubber |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPREN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lV02dM_HIPREN-EM-1712-T-TDAE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HIPREN® EM 1712 T TDAE (HIPREN EM 1723) contains 23.5% styrene bounded in polymer. It is extended with 37.5 parts (w/w) of low aromatic TDAE oil per 100.0 parts (w/w) of polymer. The rubber is produced by low temperature emulsion copolymerization process with the use of resin and fatty acids soaps as emulsifiers and is coagulated by acid. The rubber contains a staining stabiliser added during the production process. The product is without nitrosoamine. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity - ML 1+4 (100°C) | 49 | MU | ISO 289 |
| Ash Content | 0.4 | wt% | ISO 247 |
| Organic Acid | 4.5 | wt% | ISO 7781 |
| Soap | 0.5 | wt% | ISO 7781 |
| Stabilizer 1 | 0.4 | wt% | |
| Volatile Matter | 0.50 | wt% | ISO 248 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rebound Resilience | > 30 | % | ISO 4662 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time 2 | ISO 6502 | ||
| 50% : 160°C | > 6.8 | min | |
| 90% : 160°C | > 13.0 | min | |
| ETA Extract | 32.0 | wt% | ASTM D5774 |
| Scorch Time (160°C) 3 | > 3.5 | min | ISO 6502 |
| Torque 4 | ISO 6502 | ||
| Maximum : 160°C | 16.5 | dNm | |
| Minimum : 160°C | 2.40 | dNm |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bound Styrene | 23.5 | % | ISO 2453 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 64 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 13.7 | MPa | ISO 37 |
| Tensile Stress (Break) | > 19.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | > 350 | % | ISO 37 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.5 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 10.4.2.1 |
| 2 . | Standard Test Recipie: ISO 2322; Mixing Procedure: ISO 2393; Carbon Black: IRB 7; Curemeter Test: Reometar MDR 2000; Conditions: Arc 0.5° |
| 3 . | Standard Test Recipie: ISO 2322; Mixing Procedure: ISO 2393; Carbon Black: IRB 7; Curemeter Test: Reometar MDR 2000; Conditions: Arc 0.5° |
| 4 . | Standard Test Recipie: ISO 2322; Mixing Procedure: ISO 2393; Carbon Black: IRB 7; Curemeter Test: Reometar MDR 2000; Conditions: Arc 0.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 3486/20 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Sindustris PC EU5008 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| ACCUTECH™ CP0437G20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Durolon® G2530 PR001 | Unigel Plásticos | PC | Durolon® |
| TAFMER™ DF610 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |