SABIC® FORTIFY™ C0560D
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® FORTIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lTvoDI_SABICFORTIFYC0560D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® FORTIFY™ C0560D is an ethylene octene copolymer. This product is available as free flowing pellets. SABIC® FORTIFY™ C0560D is designed as a low density and high performance copolymer modifier to provide superior impact properties and flow characteristics. Typical applications are impact modifier in thermoplastic olefin compounds, footwear midsoles and wire and cable extrusion. Please take notice of specific storage and handling conditions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.863 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 36 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 64 | ASTM D2240 | |
| Shaw D, 1 sec | 17 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant | 1.90 | MPa | ASTM D638 |
| Tensile Strength (Break) | 6.10 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 1000 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 8.80 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 33.3 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -56.0 | °C | Internal method |
| Melting Temperature | 45.0 | °C | Internal method |
| Additional Information |
|---|
| All physical properties were measured on compression molded specimens. |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 520 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Sylvin 2954-65 White 1500 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ NH4030B resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Color-in™ MA301-M | Shanghai KumhoSunny Plastics Co., Ltd. | Acrylic (PMMA) | Color-in™ |
| Hax™ CAT 103 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |