Salflex 387A
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lTYzcT_Salflex-387A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Salflex 387A is a thermoplastic vulcanized rubber (TPV) product,. It can be processed by blow molding, extrusion or injection molding, and is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | 1.4 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 89 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 6.70 | MPa | ISO 37 |
| Tensile Stress (Break) | 14.7 | MPa | ISO 37 |
| Tensile Elongation (Break) | 600 | % | ISO 37 |
| Tear Strength 1 | 64 | kN/m | ISO 34-1 |
| Compression Set (125°C, 70 hr) | 68 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | 12 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | -22 | % | ISO 188 |
| Change in Shore Hardness in Air (Shore A, 150°C, 168 hr) | -1.0 | ISO 188 | |
| Change in Tensile Strength (125°C, 70 hr, in IRM 903 Oil) | -27 | % | ISO 1817 |
| Change in Tensile Strain at Break (125°C, 70 hr, in IRM 903 Oil) | -47 | % | ISO 1817 |
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 58 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature (Type B) | -59.0 | °C | ISO 812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 75.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 195 - 225 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 200 - 235 | °C | |
| Nozzle Temperature | 205 - 235 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 27.0 - 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 75.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 185 - 220 | °C | |
| Cylinder Zone 2 Temp. | 185 - 225 | °C | |
| Cylinder Zone 3 Temp. | 185 - 230 | °C | |
| Cylinder Zone 4 Temp. | 185 - 230 | °C | |
| Melt Temperature | 190 - 225 | °C | |
| Die Temperature | 185 - 235 | °C |
| Extrusion instructions |
|---|
| Blow Molding Mold Temperature: 5 to 60°C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC CKL 93 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| INSTRUC PCGF30 | Infinity LTL Engineered Compounds | PC | INSTRUC |
| Karina RED PVC COMPOUND -E 780-42/179-A-IS (C800) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 2910-90 White 1568 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2900-90 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |