15% carbon fibre reinforced Polyamide 66 injection moulding resin. Also known as: LNP* THERMOCOMP* Compound RC1003 Product reorder name: RC003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.20 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 5.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 170 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 10000 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -40°C | 3.0 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 252 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 250 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.8E+5 | ohms | IEC 60093 |
| Volume Resistivity | 1.8E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 | |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PET EN230 | Guangdong Shunde Shunyan New Material Co., Ltd. | PET | Sunny® |
| ALTECH® PP-H A 2030/250 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Braskem PE GP5550BX | Braskem | HDPE | Braskem PE |
| LNP™ THERMOCOMP™ DF008 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| LUVOCOM® 19-7277 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |