Order Products : sales@su-jiao.com
Braskem PE HC1828
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lSZ6vy_Braskem-PE-HC1828.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HC1828 is a Linear Low Density Polyethylene, 1-hexene copolymer, produced by gas phase process. Developed for cast film extrusion. Films obtained with this product show high load retention, outstanding puncture and tear resistance, excellent optical properties and are recommended for automatic application. It contains antioxidant additive. Applications: Stretch films, liners, LLDPE and HDPE blends and packages for general use. Process: HC1828 must be processed in cast extruder, adjusted to this polymer. The excellent conditions of processing in accordance with the type of used equipment, but the best results are gotten with 220 to 270°C extrusion temperature. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm | 46.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 510 | % | ASTM D882 |
| TD : Break, 25 µm | 770 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 25 µm | 147 | MPa | ASTM D790 |
| 1% Secant, TD : 25 µm | 157 | MPa | ASTM D790 |
| Dart Drop Impact 1(25 µm) | 87 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 44 | g | ASTM D1922 |
| TD : 25 µm | 150 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.0 µm) | 92 | ASTM D2457 | |
| Haze | 2.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Recommended Cast Film Extrusion Conditions: Temperature Profile: 220°C to 270°C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 600MI | Salflex Polymers Ltd. | TPO (POE) | Salflex |
| SCHULAMID® 6 GF 30 H BLACK REC | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Derakane® 411-45 | Ashland Performance Materials | Vinyl Ester | Derakane® |
| INLUBE PA66TF20IM | Infinity LTL Engineered Compounds | Nylon 66 | INLUBE |
| K-Bin Rigid PVC KB-5010 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |