TECHNYL® A 60G1 V30 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lRXGCd_TECHNYL-A-60G1-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant Polyamide PA66 reinforced with 30% of glass fibre, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.73 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.400 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11700 | 8410 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 150 | 115 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.3 | 4.2 | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.7 | 9.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 55 | 78 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 775 | -- | °C | |
| 1.60 mm | 775 | -- | °C | |
| Oxygen Index | 33 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 275 to 280 | °C | |
| Front Temperature | 280 to 285 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daelim Po1y® LH-4100BL | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| ExxonMobil™ HDPE HTA 108 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Jiangsu Meilan XXMLF3-11 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |
| Infino GI-3303LW | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |
| Sylvin 8739-65FU White 1395 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |