Stanyl® TW241F3
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lRSDKR_Stanyl-TW241F3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW241F3 is a Polyamide 46 (Nylon 46) material filled with 15% glass fiber. It is available in Asia Pacific. Important attributes of Stanyl® TW241F3 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 6100 | 2800 | MPa | |
| 120°C | 3000 | -- | MPa | |
| 160°C | 2650 | -- | MPa | |
| 180°C | 2500 | -- | MPa | |
| 200°C | 2350 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 140 | 70.0 | MPa | |
| Break, 120°C | 85.0 | -- | MPa | |
| Break, 160°C | 75.0 | -- | MPa | |
| Break, 180°C | 70.0 | -- | MPa | |
| Break, 200°C | 65.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 4.0 | 8.0 | % | |
| Break, 120°C | 12 | -- | % | |
| Break, 160°C | 12 | -- | % | |
| Break, 180°C | 12 | -- | % | |
| Break, 200°C | 12 | -- | % | |
| Flexural Modulus | 5800 | 2800 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 50 | kJ/m² | |
| 23°C | 50 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 6.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 13 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 275 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 5.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.0E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y2500C (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| ARMAMID® PA 6-4E | Poly Plastic | Nylon 6 | ARMAMID® |
| HIPOLEN P® MA 21 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| POLIMAXX SR101 | IRPC Public Company Limited | ABS | POLIMAXX |
| Infino HN-3102GH | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |