Generic EVA
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lR7qAb_Generic-EVA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic EVA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.914 - 0.982 | g/cm³ | ASTM D792 |
| 23°C | 0.922 - 0.967 | g/cm³ | ISO 1183 |
| -- | 0.920 - 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.15 - 20 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.30 - 20 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C) | 1.00 - 300 | hr | ASTM D1693 |
| Vinyl Acetate Content | 8.4 - 33.1 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 14 - 98 | ASTM D2240 | |
| 23°C | 30 - 96 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3.00 - 91.3 | MPa | ASTM D638 |
| 23°C | 50.0 - 115 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 2.71 - 18.0 | MPa | ASTM D638 |
| Yield, 23°C | 2.70 - 7.08 | MPa | ISO 527-2 |
| Fracture, 23°C | 1.38 - 20.3 | MPa | ASTM D638 |
| Fracture, 23°C | 2.00 - 26.6 | MPa | ISO 527-2 |
| 23°C | 1.90 - 8.20 | MPa | ASTM D638 |
| 23°C | 3.96 - 10.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 90 - 920 | % | ASTM D638 |
| Fracture, 23°C | 380 - 1000 | % | ISO 527-2 |
| Apparent Bending Modulus (23°C) | 29.4 - 98.1 | MPa | ASTM D747 |
| Flexural Modulus | |||
| 23°C | 2.00 - 64.4 | MPa | ASTM D790 |
| 23°C | 10.0 - 400 | MPa | ISO 178 |
| Flexural Strength (Yield, 23°C) | 40.0 - 164 | MPa | ASTM D790 |
| Coefficient of Friction | 0.49 - 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 - 64 | µm | |
| secant modulus | |||
| MD | 33.5 - 149 | MPa | ASTM D882 |
| TD | 36.6 - 125 | MPa | ASTM D882 |
| 23°C | 5.00 - 128 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Yield | 2.50 - 41.0 | MPa | ASTM D882 |
| TD : Yield | 3.63 - 30.3 | MPa | ASTM D882 |
| Yield, 23°C | 4.00 - 8.25 | MPa | ISO 527-3 |
| MD : Fracture | 14.7 - 33.7 | MPa | ASTM D882 |
| TD : Fracture | 4.30 - 36.8 | MPa | ASTM D882 |
| Fracture, 23°C | 22.0 - 39.0 | MPa | ISO 527-3 |
| 23°C | 15.0 - 27.1 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Yield | 9.0 - 410 | % | ASTM D882 |
| TD : Yield | 9.0 - 560 | % | ASTM D882 |
| MD : Fracture | 170 - 720 | % | ASTM D882 |
| TD : Fracture | 480 - 800 | % | ASTM D882 |
| Fracture, 23°C | 300 - 900 | % | ISO 527-3 |
| Dart Drop Impact | |||
| 23°C | 70 - 740 | g | ASTM D1709 |
| 23°C | 420 - 720 | g | ISO 7765-1 |
| Elmendorf Tear Strength | |||
| MD | 12 - 250 | g | ASTM D1922 |
| TD | 45 - 260 | g | ASTM D1922 |
| -- | 2.0 - 13 | N | ISO 6383-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Set | 18 - 68 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact (23°C) | 14.6 - 21.7 | J | ASTM D3763 |
| Tensile Impact Strength (23°C) | 225 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -81.3 - -69.3 | °C | ASTM D746 |
| Glass Transition Temperature | -32.0 - 0.175 | °C | ASTM E1356 |
| Vicat Softening Temperature | |||
| -- | 38.6 - 82.8 | °C | ASTM D1525 |
| -- | 38.7 - 85.6 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 58.8 - 105 | °C | |
| -- | 65.8 - 113 | °C | DSC |
| -- | 58.3 - 103 | °C | ASTM D3418 |
| -- | 68.5 - 101 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 29 - 92 | ASTM D2457 | |
| Haze | 0.70 - 8.1 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 122 - 233 | °C | |
| Mold Temperature | 20.0 - 180 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic EVAThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 134 - 160 | °C | |
| Cylinder Zone 2 Temp. | 148 - 188 | °C | |
| Cylinder Zone 3 Temp. | 156 - 235 | °C | |
| Cylinder Zone 4 Temp. | 181 - 238 | °C | |
| Cylinder Zone 5 Temp. | 181 - 238 | °C | |
| Adapter Temperature | 232 - 236 | °C | |
| Melt Temperature | 209 - 238 | °C | |
| Die Temperature | 235 - 238 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic EVAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN H2302 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Cheng Yu NGCV2 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Daplen™ EE340AE | Borealis AG | PP, Unspecified | Daplen™ |
| Gallonprene® GP550-7002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Indothene HD 54GB012 | Reliance Industries Limited | HDPE | Indothene HD |