Lupol® HI5204
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lQs0d2_Lupol-HI5204.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact, Good Weatherability Application Automotive Interior Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.1 to 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 85 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 37.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C, 6.40 mm | 44 | J/m | |
| 23°C, 6.40 mm | 200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 3.20 mm) | 130 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 30 mm/min |
| 4 . | 30 mm/min |
| 5 . | 4.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEALUTION™ 230 Peel Polymer | The Dow Chemical Company | POP | SEALUTION™ |
| VITAMIDE® BR15OR6337 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| HTA® 240 | Cytec Industries Inc. | Epoxy | HTA® |
| LNP鈩?THERMOCOMP鈩?PX85100 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| LubriOne™ PC-000/15T | PolyOne Corporation | PC | LubriOne™ |