Petrotene® PP A3 G18 FR NTLA010 PH325
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lQBFxh_Petrotene-PP-A3-G18-FR-NTLA010-PH325.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene with 18% glass fiber anti-flame, ideal for injection molding, resistant to oil, grease and various solvents, has a high tensile strength and higher HDT, and excellent dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 to 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 to 2.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Continuous Use Temperature | 100 | °C | |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CHEMIGUM® P35 | Omnova Solutions Inc. | NBR | CHEMIGUM® |
| Diaterm® B26 GF35 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 66 | Diaterm® |
| Globalprene® 3741 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Latene® 9H TES/30 | LATI S.p.A. | PP Homopolymer | Latene® |
| LUVOCOM® 1104-8928 | Lehmann & Voss & Co. | PEK | LUVOCOM® |