LNP™ LUBRICOMP™ RAL23S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lNdCGw_LNPLUBRICOMPRAL23Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing Aramid Fiber, PTFE. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound RAL-4023 HS Product reorder name: RAL23S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.24 | g/cm³ | ASTM D792 |
| -- | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.7 - 1.8 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 2.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3680 | MPa | ASTM D638 |
| -- | 3800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 89.6 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 5.9 | % | ASTM D638 |
| Fracture | 6.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3940 | MPa | ASTM D790 |
| -- | 3500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 131 | MPa | ASTM D790 |
| -- | 107 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.38 | ASTM D3702 Modified | |
| With Self-Static | 0.32 | ASTM D3702 Modified | |
| Wear Factor - Washer | 23.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 47 | J/m | ASTM D256 |
| 23°C 2 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 4 | 246 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 171 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 160 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PPR PPCO04 | Premier Plastic Resins, Inc. | PP Copolymer | PPR |
| RTP 383 TFE 20 | RTP Company | PC | RTP |
| Sindustris PC HP5005 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| OMIKRON BG 73 NAT | TECNOPOL | PP Homopolymer | OMIKRON |
| Sylvin 6407-90 Black | Sylvin Technologies Incorporated | CPE | Sylvin |