DESLEN™ DSC501M8
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lMc3r2_DESLEN-DSC501M8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLEN™ DSC501M8 is Polypropylene Mineral Filler 40% reinforced resin. It has good rigidity and heat resistance. Applications: DESLEN™ DSC501M8 is applied to electronic & electrical parts and console box which request good moldability, mechanical property and dimensional property . |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 - 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 33.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 4410 | MPa | ASTM D790 |
| Flexural Strength | 55.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 145 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 105 | °C | ASTM D648 |
| Melting Temperature | 163 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 10 SE | RTP Company | PC | RTP |
| Adell PP RR-18 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| Argothane® ST-2592-90 | Argotec LLC | TPU, Unspecified | Argothane® |
| Karina WHITE PVC COMPOUND 807-10/236-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® HB0554 | Osterman & Company | HDPE | Osterlene® |