Fibremod™ GB307HP
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lKrW4o_Fibremod-GB307HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GB307HP is a 35 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. This material shows excellent mechanical properties also at elevated temperatures. The product is available in standard black 9502. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.80 - 1.2 | % | Internal method |
| Flow direction : 2.00mm | 0.10 - 0.20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 9000 | MPa | ISO 527-2 |
| Tensile Stress | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 8000 | MPa | ISO 178 |
| Flexural Stress | 163 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 54 | kJ/m² | ISO 179/1eU |
| 23°C | 54 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 153 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SA5007 | Spartech Polycom | ABS | Spartech |
| StarMediflex P 7030-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| TPUCO® TPUE-UEH95 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Axiall PVC 9211 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| HiFill® TPU/I GF40 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |