NORYL™ HNA055 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lK9Zga_NORYLHNA055resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| >PPE+PS-HI< Autoclavable engineering thermoplastic. Biocompatible per ISO10993 (color dependent). |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 6.2 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 5.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.23 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3250 | MPa | ASTM D638 |
| -- | 2410 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 67.9 | MPa | ASTM D638 |
| Yield | 61.8 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.5 | MPa | ASTM D638 |
| Fracture | 57.6 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.8 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/50 |
| Fracture 5 | 16 | % | ASTM D638 |
| Fracture | 13 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2540 | MPa | ASTM D790 |
| -- 7 | 2490 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 107 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 27 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 290 | J/m | ASTM D256 |
| -30°C 10 | 15 | kJ/m² | ISO 180/1A |
| 23°C 11 | 25 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 54.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 147 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 148 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 168 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 169 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 9.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 260 - 304 | °C | |
| Middle Temperature | 271 - 310 | °C | |
| Front Temperature | 282 - 316 | °C | |
| Nozzle Temperature | 293 - 316 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-5033LT | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| SLOVAMID® 66 GF 35 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Derakane® 470HT-400 | Ashland Performance Materials | Vinyl Ester | Derakane® |
| FLEXITEQ™ F65A111UV | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Petrotene® PP B3 TZ PRTA011 PH347 MSP | Petropol Industry and Trade of Polymers LTDA | PP Copolymer | Petrotene® PP |