TOTAL Polyethylene HDPE 2287
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lIyVwb_TOTAL-Polyethylene-HDPE-2287.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene 2287 is a High Density Polyethylene material. It is available in North America. Important attributes of TOTAL Polyethylene 2287 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 10 | g/10 min | |
| 190°C/5.0 kg | 0.32 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Secant Modulus 1 | ASTM D882A | ||
| 2% Secant, MD : 20 µm, Blown Film | 841 | MPa | |
| 2% Secant, TD : 20 µm, Blown Film | 910 | MPa | |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, 20 µm, Blown Film | 36.5 | MPa | |
| TD : Yield, 20 µm, Blown Film | 34.5 | MPa | |
| MD : Break, 20 µm, Blown Film | 63.4 | MPa | |
| TD : Break, 20 µm, Blown Film | 67.6 | MPa | |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Break, 20 µm, Blown Film | 300 to 500 | % | |
| TD : Break, 20 µm, Blown Film | 300 to 500 | % | |
| Dart Drop Impact (20 µm, Blown Film) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, Blown Film | 24 | g | |
| TD : 20 µm, Blown Film | 120 | g | |
| Water Vapor Transmission Rate (38°C, 20 µm, Blown Film) | 12 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001 | PolyOne Corporation | PC | Stat-Tech™ |
| Axiall PVC 5006 Natural | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Elastron® V V101.A50.N | Elastron USA, Inc. | TPV | Elastron® V |
| KOPA® KN133G33BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| ISOTHANE® 1070A-S | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |