Solarkote® P610
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Solarkote® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lIqUF8_Solarkote-P610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solarkote® P610 is a Polymethyl Methacrylate Acrylic product. It is available in Europe or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.80 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 69 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1320 | MPa | ASTM D638 |
| Tensile Strength (Break) | 20.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 85 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Flexural Strength (Break) | 33.1 | MPa | ASTM D790 |
| Taber Abrasion Resistance | ASTM D1044 | ||
| 100 Cycles, 500 g | 0.00100 | mg | |
| 500 Cycles, 500 g | 0.0105 | mg | |
| 1000 Cycles, 500 g | 0.0165 | mg | |
| 2000 Cycles, 500 g | 0.0355 | mg |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 51.7 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 68.9 | °C | ASTM D1525 1 |
| -- | 58.3 | °C | ASTM D1525 2 |
| CLTE - Flow | ASTM E831 | ||
| -18°C | 1.2E-4 | cm/cm/°C | |
| -7°C | 1.2E-4 | cm/cm/°C | |
| 24°C | 1.4E-4 | cm/cm/°C | |
| 38°C | 1.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH301G6NT | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| Sinpolene TPP2020 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | Sinpolene |
| Adiprene® LF 1800A | Chemtura | PUR-Ester/TDI | Adiprene® |
| Latigloss 57 G/60 F2 | LATI S.p.A. | PPA | Latigloss |
| 3M™ Dyneon™ PTFE Compound 310192004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |