SCHULAMID® 66 GBF 3020
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lITKRs_SCHULAMID-66-GBF-3020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber and glass bead reinforced Polyamide 66 with high tensile strength and dimensional stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 2.0 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 220 | 140 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7600 | 4400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | 80.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | 10 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 6000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 190 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 4.5 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 14 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 40 | 60 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 240 | -- | °C | ISO 306/A50 |
| -- | 235 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (140°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | |
| 3.00 mm | -- | 650 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® EL-3800E | Sumitomo Bakelite Co., Ltd. | Epoxy | SUMILITE® |
| Mylar® A (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Electrafil® PC CF20 FR IM BK | Techmer Engineered Solutions | PC | Electrafil® |
| PEEK-OPTIMA® Image Contrast (Low radiopacity) | Invibio Inc. | PEEK | PEEK-OPTIMA® |
| Sylvin 4299-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |