Generic PP, Unspecified - Glass Bead
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lI88cD_Generic-PP-Unspecified---Glass-Bead.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass Bead This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.950 - 1.48 | g/cm³ | ASTM D792 |
| 23°C | 1.05 - 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (23°C) | 0.50 - 1.8 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.019 - 0.031 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1100 - 5860 | MPa | ASTM D638 |
| 23°C | 1500 - 3250 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 19.3 - 100 | MPa | ASTM D638 |
| Fracture, 23°C | 15.9 - 45.0 | MPa | ASTM D638 |
| Fracture, 23°C | 15.0 - 25.5 | MPa | ISO 527-2 |
| 23°C | 24.9 - 33.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 9.8 - 10 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 14 | % | ASTM D638 |
| Fracture, 23°C | 3.6 - 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1200 - 4200 | MPa | ASTM D790 |
| 23°C | 1880 - 2220 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 27.6 - 71.0 | MPa | ASTM D790 |
| 23°C | 35.0 - 40.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 25 - 43 | J/m | ASTM D256 |
| 23°C | 2.1 - 4.2 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 250 - 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 111 - 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 - 122 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 56.0 - 103 | °C | ISO 75-2/A |
| CLTE - Flow | 3.8E-5 - 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+12 - 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 20 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 199 - 246 | °C | |
| Middle Temperature | 210 - 246 | °C | |
| Front Temperature | 210 - 246 | °C | |
| Processing (Melt) Temp | 211 - 240 | °C | |
| Mold Temperature | 40.2 - 50.7 | °C | |
| Injection Pressure | 85.9 - 86.4 | MPa | |
| Back Pressure | 0.258 - 0.517 | MPa | |
| Screw Speed | 45 - 70 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass BeadThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4900 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| YUNCON® N270 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNCON® |
| Xuchuan XCS-3935 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Fainplast PVC PK 1080 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Durethan® BKV 30 W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |