| Staramide BG3ST43 is an Impact Modified and Glass Fiber Reinforced Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.80 to 1.2 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 5.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2 | ISO 180/1A | ||
| -40°C | 7.0 | kJ/m² | |
| -20°C | 12 | kJ/m² | |
| 23°C | 18 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 200 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 160 | °C | ISO 75-2/Ae |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 80*10*4 |
| 3 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GTPO8102BA-H NATURAL | S&E Specialty Polymers, LLC | TPO (POE) | S&E Wire & Cable |
| Next Nylon 66 Prime Series PGF25-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| NORYL™ PKN4775F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Huafon EP158N | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| LNP™ COLORCOMP™ J1000E compound | SABIC Innovative Plastics Europe | PESU | LNP™ COLORCOMP™ |