Elexar® EL-8732R

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Elexar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lHOMCL_Elexar-EL-8732R.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Elexar EL-8732R is a high performance, flame retardant thermoplastic elastomer designed for electrical applications requiring flexibility over a wide termperture range. Elexar EL-8732R is a high durometer grade that is UV stablized and RoHS compliant. This grade is UL listed and is suitable for both injection molding and extrusion.

General Information
Features	High elasticity High tensile strength Good UV resistance Good heat aging resistance Good flexibility Good coloring Medium liquidity Halogenated Ozone resistance Good weather resistance Sunlight resistance, 720 hours General Extended tensile rate Flame retardancy
Uses	Underground cable Cable sheath Electrical wire sheath material Electrical conductor insulation material Wire and cable applications Wire sheath Industrial cable insulation material Connector cord sheath Terminal cable sheath material
Agency Ratings	UL 1581
RoHS Compliance	RoHS compliance
UL File Number	QMTT2.E73402
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.18	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	10	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	81		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ASTM D412
100% strain, 0.508mm ²	3.24	MPa	ASTM D412
300% strain, 0.508mm ³	4.76	MPa	ASTM D412
Tensile Strength (Yield, 0.508 mm)	12.1	MPa	ASTM D412
Tensile Elongation (fracture, 0.508mm)	650	%	ASTM D412

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (136°C, 168 hr)	-10	%	ASTM D573
Change in Ultimate Elongation in Air (136°C, 168 hr)	-7.0	%	ASTM D573
Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil)	-4.0	%	ASTM D471
Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil)	2.0	%	ASTM D471

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	105	°C	UL 1581
Brittleness Temperature	-60.0	°C	ASTM D746
RTI Elec	50.0	°C	UL 746
RTI Imp	50.0	°C	UL 746
RTI	50.0	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity			ASTM D257
23°C	1.4E+16	ohms·cm	ASTM D257
50°C	6.5E+14	ohms·cm	ASTM D257
Dielectric Strength	25	kV/mm	ASTM D149
Dielectric Constant (1 kHz)	2.40		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.00 mm)	V-2		UL 94
Oxygen Index	23	%	ASTM D2863

Injection	Nominal Value	Unit
Rear Temperature	199 - 216	°C
Middle Temperature	213 - 221	°C
Front Temperature	221 - 227	°C
Nozzle Temperature	221 - 229	°C
Processing (Melt) Temp	221 - 229	°C
Mold Temperature	25.0 - 65.6	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Moderate-Fast
Back Pressure	0.172 - 0.345	MPa
Screw Speed	50 - 100	rpm
Cushion	3.81 - 25.4	mm

Injection instructions
Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C).

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	193 - 210	°C
Cylinder Zone 2 Temp.	199 - 216	°C
Cylinder Zone 3 Temp.	213 - 221	°C
Cylinder Zone 5 Temp.	221 - 227	°C
Die Temperature	221 - 229	°C

Extrusion instructions
Screw Speed: 30 to 100 rpm

Note Message
1 .	die cut from extruded tapes
2 .	Mouth die C, 510mm/min
3 .	C mold, 510mm/min

Resin Grade	Manufacturer	Category	Trademark
MTEGRITY™ PS General Purpose GS230WC	M. Holland Company	PS (Specialty)	MTEGRITY™ PS General Purpose
UBE Nylon P7115 U	UBE Engineering Plastics, S.A.	Nylon 612	UBE Nylon
NuSil MED-4211	NuSil Technology	Silicone	NuSil
COPYLENE® CH110	Phillips 66	PP Homopolymer	COPYLENE®
RTP ESD 1385 HF	RTP Company	PPS	RTP