BorLite™ OPE792
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | BorLite™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lGqMDX_BorLite-OPE792.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BorLite OPE792 is a high molecular weight linear low density polyethylene film grade providing high melt strength for good processing behaviour of primary films on blown film technology as well as excellent draw down on mono directional orientation (MDO) lines. MDO-films made of this product are characterised by very high toughness and balanced MD/TD tear resistance. BorLite OPE792 has been developed especially for property-enhancement of blown films through mono-directional orientation (MDO technology). BorLite OPE792 is recommended for:
BorLite OPE792 contains antioxidant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 22 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 900 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 900 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 170 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 18.0 | MPa | ISO 527-3 |
| MD : 25 µm, blown film | 170 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 19.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 30 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 750 | % | ISO 527-3 |
| Dart Drop Impact (25 µm) | 790 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 25.0 µm | 165.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 170.0 | kN/m | ISO 6383-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Energy to Break (25.0 µm) 2 | 450 | J/cm | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 101 | °C | ISO 306/A |
| Melting Temperature | 124 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.0 µm, Blown Film) | 14 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties are measured on a 25 µm MD-oriented film sample, DDR 1:6. Primary film produced on a 70 mm extruder, BUR=1:2.7, Die gap: 1.2 mm, FLH 2-4 DD, thickness 150 µm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Melt Temperature | 190 - 210 | °C | |
| Die Temperature | 190 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ecollent™ PPC | Lucent Polymers, Inc. | PP, Unspecified | Ecollent™ |
| Electrafil® ABS CF10 A1 | Techmer Engineered Solutions | ABS | Electrafil® |
| KOPA® KN173HI4 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Karina COMP. PVC WHITE -E 786-10/332-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| LNP™ THERMOCOMP™ D551 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |