Geon™ CPVC LC510
| Category: | CPVC , Chlorinated Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ CPVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lGo3GU_Geon-CPVC-LC510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon LC510 CPVC is an extrusion grade rigid compound. LC510 offers excellent chemical resistance and is designed for applications where enhanced resistance at elevated temperatures is needed. LC510 demonstrates ease of processing with excellent thermal stability. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, 3.18 mm) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 3.18 mm, Compression Molded) | 2250 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 23°C, 3.18 mm, Compression Molded) | 53.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.18 mm) | 24 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 2430 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.18 mm) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drop Impact Resistance 4(23°C) | 66.7 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 106 | °C | |
| 0.45 MPa, Annealed, 3.18 mm | 111 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 92.8 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 105 | °C | |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 to 199 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | Procedure A, C.125 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niretan B EXL | Soredi S.p.a. | Nylon 66 | Niretan B |
| Chemlon® 109-13 GHU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hangzhou Plastic PS/PVDC | Hangzhou Plastic Industry Co., Ltd. | Film, PS/PVDC | Hangzhou Plastic |
| Moplen EP5079 | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Sylvin 9940-75 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |