MAJORIS ET311 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lGYmhS_MAJORIS-ET311---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ET311 - 8229 is a mineral filled polypropylene compound intended for injection moulding. ET311 - 8229 has been developed especially for the automotive under hood applications requiring excellent long-term heat stability. The good flowability of ET311 - 8229 makes it very easy to process for complicated parts with long flow paths. The product is available in both black (ET311 - 8229) and natural (ET311) but other colours can be provided on request. Products requiring good long-term heat resistance, very heat distortion temperature, excellent rigidity, low shrinkage and high dimensional stability can suitably be made from ET311 - 8229. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 11 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 51 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 79.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.2 | kJ/m² | ISO 179/1eA |
| 23°C | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 11 | kJ/m² | ISO 179/1eU |
| 23°C | 26 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 131 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/A |
| -- | 92.0 | °C | ISO 306/B |
| Thermal stability (150°C) | > 700.0 | hr |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging | DIN 75201 | ||
| 100°C/16h | 2.0E-4 | g | DIN 75201 |
| 100°C/3h | 96 | % | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | 22.0 | µgC/g | VDA 277 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trovidur® PHT | Röchling Engineering Plastics SE & Co. KG | CPVC | Trovidur® |
| Clyrell RC215M | LyondellBasell Industries | PP Random Copolymer | Clyrell |
| OKITEN® 245 A | DIOKI d.d. | LDPE | OKITEN® |
| SABIC® LDPE PCG06 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Purell RP271M | LyondellBasell Industries | PP Random Copolymer | Purell |