LNP™ LUBRICOMP™ DL004 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lFWns3_LNP-LUBRICOMP-DL004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DL004 is a compound based on Polycarbonate resin containing 20% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4040 Product reorder name: DL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.64 | % | ISO 294-4 |
| Flow : 24 hr | 0.59 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.36 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2080 | MPa | ASTM D638 |
| -- | 2050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/5 |
| Break 3 | 39.0 | MPa | ASTM D638 |
| Break | 39.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.2 | % | ASTM D638 |
| Yield | 5.9 | % | ISO 527-2/5 |
| Break 5 | 29 | % | ASTM D638 |
| Break | 29 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2060 | MPa | ASTM D790 |
| -- 7 | 1930 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 73.8 | MPa | ASTM D790 |
| -- | 63.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.21 | ||
| Wear Factor - Washer | 7.50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 8 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1900 | J/m | ASTM D4812 |
| 23°C 9 | 180 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 24.8 | J | ASTM D3763 |
| 23°C, Total Energy | 24.8 | J | ASTM D3763 |
| -- | 21.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 129 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer S40H | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| RAMSHINE PV111 | Polyram Ram-On Industries | ABS | RAMSHINE |
| Styrolution PS 5410 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| T-Blend® TPR-F78B | TSRC Corporation | SEBS | T-Blend® |
| ALTECH® PC + ABS ECO 1000/500 | ALBIS PLASTIC GmbH | PC+ABS | ALTECH® PC + ABS |