Order Products : sales@su-jiao.com
Retpol® 3007 FC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lF4lOy_Retpol-3007-FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXTRON 3007 FC is a 30% glass fibre reinforced polypropylene compound. It is a medium flow injection moulding grade developed for components requiring a combination of high rigidity, low shrinkage and improved creep resistance. It has been manufactured in accordance with Australian Standard AS 2070-1999 "Plastic Material for Food Contact Use". The ingredients used in this formulation are referenced in the US Code of Federal Regulations, Volume 21, parts 170-199. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 113 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 80 | ||
| Shore D, 15 sec, 3.00 mm | 75 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 6100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 34 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 155 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 135 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYPET VNT 930 | Lavergne Group | PET | VYPET |
| YUPLENE® R940F | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Nypol® PA A3 G25 PRTA010 NR438 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LubriOne™ PC-20GF/13T-2S NATURAL | PolyOne Corporation | PC | LubriOne™ |
| Petrotene® PP A3 T20 PRTA010 PH379 MSP | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |