Zytel® FG7301 NC010
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lEY0q4_ZytelFG7301NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Polyamide 6 |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 9.5 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 3.0 | -- | % | ISO 62 |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | -- | % | ISO 527-2 |
| Flexural Modulus | 2300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | No Break | -- | ISO 179/1eU | |
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 6.0 | -- | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | -- | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 270 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec | |
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 GB 30 | RTP Company | Nylon 66 | RTP |
| PRL TP-FR-IM-(color)-3 | Polymer Resources Ltd. | PBT | PRL |
| T-Blend® 5531N-SI | TSRC Corporation | TPE | T-Blend® |
| New-prene™ 6165B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Aurora PVC AP2261 | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |