Leona™ 54G33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lD6Gi0_Leona-54G33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 54G33 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 54G33 include automotive, engineering/industrial parts, fabrics/fibers and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.9 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.9 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 93 | 68 | ||
| R-Scale | 120 | 110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9700 | 6100 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 183 | 113 | MPa | ISO 527-2 |
| -- | 181 | 118 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 3.0 | 7.0 | % | ASTM D638 |
| Break, 23°C | 4.0 | 9.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 9100 | 5000 | MPa | ASTM D790 |
| 23°C | 9000 | 5300 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 289 | 167 | MPa | ASTM D790 |
| 23°C | 270 | 165 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 12 | 19 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 98 | 98 | kJ/m² | ISO 179 |
| Notched Izod Impact | 140 | 200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 230 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 31 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProtoGen 18120 | DSM Somos® | Unspecified | ProtoGen |
| SEETEC LLDPE UL814 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Teldene® H11BF | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| Xuchuan XCW-120E | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| LEXAN™ HPS2REU resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |