Nypol® PA A3 G30 M2 N1 NTLA014 NR353 MSP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lCmtAA_Nypol-PA-A3-G30-M2-N1-NTLA014-NR353-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 30% fo fiberglass, lubricated with molybdenum disulfide and graphite, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 140 | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 10000 | 7000 | MPa | ASTM D790 |
| Flexural Strength | 238 | 205 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 80 | 90 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® FD-0348 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE | VENELENE® |
| VITAMIDE® AS30WT6020 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| LNP™ THERMOCOMP™ UC006H compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Petrothene® NA247000 | LyondellBasell Industries | LDPE | Petrothene® |
| PLEXIGLAS® Sheet Optical 0Z024 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |