TERRAMAC TE-2000

Category: PLA , Polylactic Acid
Manufacturer: UNITIKA Plastics Division
Trademark: TERRAMAC
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: lCm4yO_TERRAMAC-TE-2000.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
TERRAMAC TE-2000 is a Polylactic Acid (PLA) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of TERRAMAC TE-2000: Eco-Friendly/Green.

Typical applications include:
  • Business/Office Goods
  • Consumer Goods
  • Containers
  • Electrical/Electronic Applications
  • Trays/Racks
General Information
Features
  • Biodegradable
  • General Purpose
  • Renewable Resource Content
Uses
  • Consumer Applications
  • Containers
  • Electrical/Electronic Applications
  • Stationary Supplies
  • Support Trays
Appearance
  • Clear/Transparent
Forms
  • Pellets
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Density 1.25g/cm³ISO 1183
Molding Shrinkage 0.30 to 0.50%ISO 294-4
MechanicalNominal ValueUnitTest Method
Tensile Stress (Break)63.0MPaISO 527-2
Tensile Strain (Break)4.0%ISO 527-2
Flexural Modulus 4300MPaISO 178
Flexural Stress 106MPaISO 178
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength 1.6kJ/m²ISO 179
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature (0.45 MPa, Unannealed)58.0°CISO 75-2/B
Melting Temperature 170°C
InjectionNominal ValueUnit
Rear Temperature 130 to 170°C
Middle Temperature 180 to 220°C
Front Temperature 180 to 220°C
Nozzle Temperature 180 to 220°C
Processing (Melt) Temp < 240°C
Mold Temperature 10.0 to 30.0°C
Back Pressure 0.490 to 1.47MPa
Resin Grade Manufacturer Category Trademark
RTP 1000 TFE 20 FR A RTP Company PBT RTP
BCC Resins BC 8405 BCC Products Inc. PUR, Unspecified BCC Resins
DynaMix™ 2045-BRD Polymer Dynamix Nylon 66 DynaMix™
KRALASTIC® ST-100 Nippon A&L Inc. ABS KRALASTIC®
3M™ Dyneon™ Fluoroelastomer FE 5620N 3M Advanced Materials Division Fluorelastomer 3M™ Dyneon™ Fluoroelastomer