TECHNYL® A 402H1 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lCCIuA_TECHNYL-A-402H1-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 402H1 Natural is an unreinforced polyamide 66, very high viscosity, heat stabilized, for extrusion and injection moulding. This product is available in natural color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption (Saturation, 23°C) | 1.5 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1300 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 80.0 | 60.0 | MPa | |
| Break | 60.0 | -- | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 8.0 | 30 | % | |
| Break | 60 | 250 | % | |
| Flexural Modulus | 2800 | 1300 | MPa | ISO 178 |
| Flexural Stress | 140 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 6.0 | 35 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | 26 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 475 | 575 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Cylinder Zone 1 Temp. | 260 to 270 | °C | |
| Cylinder Zone 3 Temp. | 270 to 280 | °C | |
| Cylinder Zone 5 Temp. | 280 to 290 | °C | |
| Die Temperature | 280 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9825-60 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® CP-28136 | Teknor Apex Company | TPE | Monprene® |
| CET® 123 | Resirene, S.A. de C.V. | Acrylic (SMMA) | CET® |
| LEXAN™ 4795R resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| Zytel® RS LC4601 BK010 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |