GLAMIDE® TY-145TZ
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lAbw8k_GLAMIDE-TY-145TZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®TY-145TZ is a polyamide 6 (nylon 6) product, which contains a 25% mineral filler. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.33 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 15 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 - 0.30 | -- | % | ASTM D955 |
| 3.00 mm | 0.40 - 0.80 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.80 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.7 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 107 | 102 | MPa | ASTM D638 |
| Yield, 23°C | 85.0 | 58.0 | MPa | ASTM D638 |
| Yield, 80°C | 45.0 | 36.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 8000 | 7000 | MPa | ASTM D790 |
| 23°C | 6800 | 4600 | MPa | ASTM D790 |
| 80°C | 3700 | 1500 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 168 | 158 | MPa | ASTM D790 |
| Yield, 23°C | 140 | 93.0 | MPa | ASTM D790 |
| Yield, 80°C | 78.0 | 53.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 97.0 | 66.0 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles, CS-17 Wheel) | 30.0 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 54 | 68 | J/m | ASTM D256 |
| 23°C | 80 | 260 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 207 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 155 | -- | °C | ASTM D648 |
| CLTE - Flow | 5.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | 17 | kV/mm | ASTM D149 |
| Arc Resistance | 130 | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SGF 45 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| DOW™ MDPE DMDA-8962 NT 7 | The Dow Chemical Company | MDPE | DOW™ MDPE |
| Advanced Composites FNS-175S | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Baytec® 352 (76A) | Covestro - PUR | TSU | Baytec® |
| apilon 52c® C S60 LV | API SpA | TPU-Polyester | apilon 52c® |