CALIBRE™ 200-3
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l9gWUZ_CALIBRE-200-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 200-3 polycarbonate resin is produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. This resin provides excellent impact resistance, heat distortion resistance and optical clarity as well as high melt strength for sheet extrusion applications. Available in natural color only. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 74 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2480 | MPa | ASTM D638 |
| -- | 2480 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 72.4 | MPa | ASTM D638 |
| Break | 72.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2410 | MPa | ASTM D790 |
| -- 6 | 2410 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 96.5 | MPa | ASTM D790 |
| -- 8 | 96.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 960 | J/m | ASTM D256 |
| 23°C | 93 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 9(23°C, Total Energy) | 93.8 | J | ASTM D3763 |
| Tensile Impact Strength | 630 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 146 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 132 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 143 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 151 | °C | ISO 306/B50, ASTM D1525 10 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 11 | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index 12 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Method I (3 point load), 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 3.39 m/sec |
| 10 . | Rate A (50°C/h), Loading 2 (50 N) |
| 11 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2560F | Teknor Apex Company | TPE | Telcar® |
| Sylvin 7833-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Adell Polyamide BA-36 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| KEBATER® PBT B510 | BARLOG plastics GmbH | PBT | KEBATER® |
| LNP™ LUBRICOMP™ AL002 compound | SABIC Innovative Plastics | ABS | LNP™ LUBRICOMP™ |