Daplen™ EE189HP
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l9HVC2_Daplen-EE189HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EE189HP is a 15% mineral filled polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.95 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 1700 | MPa | ISO 527-2 |
| Tensile Stress | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 1750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 26 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 95 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 94.0 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 128 | °C | ISO 306/A |
| -- | 51.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging 2(100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 210 - 250 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 16 h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2200H0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Spartech Polycom PP5140F B1 | Spartech Polycom | PP, Unspecified | Spartech |
| SUPREME GPPS SC203L | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Honeywell PCTFE P900TR | Honeywell | PCTFE | Honeywell PCTFE |
| Karina IVORY PVC COMP -E 835-35/ 1-ERYB-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |