AKROMID® B3 GF 40 9 RM-M natural (3414)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l95Uwg_AKROMID-B3-GF-40-9-RM-M-natural-3414-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 40 9 RM-M natural (3414) is a 40% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength, limited moisture absorption and light inherent color. Applications are housings and other dimensional stable parts in the automotive and electronic industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Spiral Flow | 56.0 | cm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 72 | kJ/m² | |
| 23°C | 76 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 208 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 160 | °C | ISO 75-2/C |
| Melting Temperature 1 | 225 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 40 | % | ISO 1172 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU C665MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| TRANSMARE® 14CGF40-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Niche PA6GF13N | Niche Polymer, LLC | Nylon 6 | Niche |
| Latamid 66 H2 G/25-V0KB3 | LATI S.p.A. | Nylon 66 | Latamid |
| POCAN® B 1305 000000 | LANXESS GmbH | PBT | POCAN® |