Alkathene® Ultra LDJ226
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l8gFoy_Alkathene-Ultra-LDJ226.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDJ226 is a low density polyethylene designed predominantly for use in bundle shrink film and a variety of low gauge (20 - 50µm) general purpose applications where a medium slip film is required. LDJ226 is formulated with a process stabilisation and antiblock package and contains antistatic additives. LDJ226 is intended for use in a wide range of shrink and general purpose film applications typically of the thickness 20 to 50µm. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 32 µm, blown film | 160 | MPa | ASTM D882 |
| 2% secant, TD : 32 µm, blown film | 190 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 32 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 16.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 270 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 740 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 390 | g | ASTM D1922 |
| TD : 32 µm, blown film | 170 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 32.0 µm, blown film) | 71 | ASTM D2457 | |
| Haze (32.0 µm, blown film) | 7.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GF-91-102-2 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Sinvicomp DBS3607 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Novomer NB-20 | Novomer, Inc. | PC | Novomer |
| Delrin® 100KM NC000 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| HYPERIER® IP1306B | LG Chem Ltd. | Nylon, Unspecified | HYPERIER® |