ELIX™ ABS P2H-AT
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ELIX Polymers, S. L. |
| Trademark: | ELIX™ ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l8UFbP_ELIX-ABS-P2H-AT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELIX ABS P2H-AT Standard impact strength, easy flowing, high gloss, contains antistatic additive ISO Shortname: ISO 2580-1 -ABS 0, MGZ, 095-30-16-25 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 2580) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 37.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.40 to 0.60 | % | |
| Flow | 0.40 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 44.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 2.1 | % | |
| Break, 23°C | > 15 | % | |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2200 | MPa | |
| 1000 hr | 1500 | MPa | |
| Flexural Modulus 2(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 16 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.00 | ||
| 23°C, 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 5.5E-3 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(2.00 mm) | 60 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec | ISO 294 |
| Note Message | |
|---|---|
| 1 . | 60x60x2 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | US - FMVSS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 6013M-07 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Nylene® NX4004A HS BLACK | Custom Resins Group | Nylon 6 | Nylene® |
| Karina BLACK PVC COMPOUND 920D48/1-CY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnFlex™ V 3085A-S0098 | PolyOne Corporation | TPE | OnFlex™ |
| DAI-EL™ G-704 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |